Product Details:
|
| Color: | Light Yellow Liquid | Flash Point: | High |
|---|---|---|---|
| Odor: | Less | Product Name: | Polyurethane Prepolymer For PU Elastomer |
| Shelf Life: | 1 Year In The Original Drum | Process Temperature: | 80 Degree C |
| Specific Gravity: | 1.1 | Stability: | Stable |
| Storage Conditions: | Cool And Dry Place | Appearance: | Liquid In The Room Temperature |
| Application: | To Make PU Screen, Castor Wheels Etc . | Physical Performation: | Excellent |
| Highlight: | Polyurethane Pre Polymer Shore A60,PPG TDI Series Polyurethane Pre Polymer,Polyurethane Pre Polymer Shore D60 |
||
PPG/TDI series Polyurethane Pre-polymer shore A60- shore D60
Polyether-TDI PU Pre-polymers
Application:It can be used to make rods, caster wheels, rollers,
Sealing rings, sieve plates and other polyurethane elastomers.
Characteristics:The finished products have good abrasion resistance, Water resistance, germ proof, excellent mechanical properties, color regulating by adding pigment.
Process Points:After the performed polymer vacuum degassing in 80～85 ℃, blending with melted MOCA, vacuum degassing, casting, vulcanization moulding. It is apply to manual or casting machine.
Storage:Store in a cool and dry place,If you can ’t use it up at a time, filling nitrogen gas and then sealing it. The storage time of original packing is 6 month.
Packing:20Kg/drum or 200Kg/drum
| Type | JY2122A | JY2125A | JY2128A | JY2133A | JY2138A | JY2143 |
| NCO content % | 2.2±0.2 | 2.5±0.2 | 2.8±0.2 | 3.3±0.2 | 3.8±0.2 | 4.3±0.2 |
| Appearance at 20℃ | Colorless transprent liquid | |||||
|
MOCA/g (100g prepolymer) |
6.5 | 7.4 | 8.3 | 9.8 | 11.2 | 12.7 |
| Viscosity (85℃) /mPa · s | 1200 | 700 | 600 | 650 | 500 | 230 |
| Mixing Temperature /℃ | 80/115 | 85/115 | 85/115 | 80/120 | 80/115 | 80/115 |
| Gel time/min | 14-20 | 11-14 | 8-12 | 6-9 | 5-8 | 4-6 |
| Post cure time(100 ℃)/h | 16 | 16 | 16 | 16 | 16 | 16 |
| Hardness(Shore A) | 62 | 65 | 70 | 75 | 80 | 85 |
| 100% Modulus /MPa | 2 | 2 | 3 | 3 | 4 | 4 |
| 300% Modulus /MPa | 3 | 4 | 5 | 6 | 9 | 10 |
| Tensile strength /MPa | 8 | 10 | 12 | 14 | 15 | 22 |
| Elongation at break/ % | 700 | 650 | 600 | 500 | 480 | 450 |
| Tear Strength (without Nick) | 42 | 45 | 50 | 63 | 68 | 65 |
| Rebound / % | 60 | 55 | 50 | 45 | 45 | 35 |
| Specific gravity (25℃) (g/ cm3) | 1.1 | 1.07 | 1.07 | 1.08 | 1.1 | 1.08 |
| Abrasion loss /mm³ | 150 | 160 | 150 | 130 | 135 | 140 |