Product Details:
|
| Mold Resistance: | Good | Hardness: | 95A |
|---|---|---|---|
| Elongation: | 500% | Appearance: | Granules |
| Name: | Thermoplastic Polyurethane Resin | Tear Strength: | 120 KN/m |
| Tensile Strength: | 47 Mpa | UV Resistance: | Good Anti Yellowing |
| Highlight: | Polyether PTMEG-MDI TPU,TPU Raw Materials Hardness 95A,TPU Raw Materials Granules |
||
Polyether PTMEG-MDI TPU with good mold resistance with hardness 95A
K-1295AU PTMEG system TPU 95A
◆ Description
K-1295AU is a Polyether PTMEG-MDI TPU with good mold resistance which is made from PTMEG and MD with hardness 95A. These finished products have excellent water resistance,Mold resistance, anti-yellowing resistance; They have good resilience and flexibility in the low working temperature. These materials can be processed by injection, extrusion,modified etc. This high quality TPU is widely used for the tube, film, Cable Protective Cover, fire hose, Fabric coating, and some sports products.
◆ Technical data
| Item | Test method | Unit | Result |
| Hardness | ISO 868 | Shore A | 95 |
| Density | ISO 1183-1 | g/cm3 | 1.16 |
Physical property
| 100% modulus | DIN 53504 | MPa | 12 |
| 300% modulus | DIN 53504 | MPa | 22.0 |
| Tensile strength | DIN 53504 | MPa | 47.0 |
| Tear strength | ISO 34-1 | N/mm | 120.0 |
| Elongation at break | DIN 53504 | % | 500 |
| DIN abrasion loss | ISO4649 | mm3 | -- |
| Process temp. | — | °C | 170～200 |
◆ Package
25Kg/bag
Process advisement (Dry the granules 3-4 hours at 80-90℃ before using)
|
Injection ℃ |
Item |
Recommended Temperature Extrusion ℃ |
Item |
| 195-220 | nozzle | 185-195 | nozzle |
| 190 | metering zone | 190 | connector |
| 185 | Compression zone | 185 | metering zone |
| 180 | Feeding zone | 180 | Compression zone |
| 85 | Injection pressure(KG) | 175-185 | Feeding zone |
◆ Storage
It must be stored in a dry and cool place to prevent moisture absorption and sun exposure. Safety data refer to MSDS